Inconel 601 is a nickel-chromium alloy optimized for high-temperature oxidation resistance, suitable for furnace parts, heat treating equipment, and exhaust systems.
Element | Content (%) |
Nickel (Ni) | ≥ 63.0 |
Chromium (Cr) | 21.0 – 25.0 |
Iron (Fe) | 10.0 – 15.0 |
Aluminum (Al) | 1.0 – 1.7 |
Manganese (Mn) | ≤ 1.00 |
Silicon (Si) | ≤ 0.50 |
Carbon (C) | ≤ 0.10 |
Sulfur (S) | ≤ 0.015 |
Property | Value (Typical) | Unit | Condition |
Tensile Strength (Ultimate) | ≥ 650 | MPa | Annealed |
Yield Strength (0.2% Offset) | ≥ 275 | MPa | Annealed |
Elongation (in 50 mm) | ≥ 30 | % | ASTM B168 |
Hardness (Brinell) | ≤ 160 | HB | |
Density | 8.19 | g/cm³ | Room Temp |
Melting Range | 1320 – 1380 | °C | |
Modulus of Elasticity | ~204 | GPa | Room Temp |